Title: | The effects of huntite–hydromagnesite inclusion in acrylate-based polymer paste coating process on some textile functional performance properties of cotton fabric | Authors: | Çamlıbel, Nurhan Onar Avinc, Ozan Arık, Buket Yavaş, Arzu Yakın, İsmail |
Keywords: | Antibacterial Coating Cotton Flame retardancy Huntite Huntite–hydromagnesite Hydromagnesite Knife over roll coating Polyacrylate UV protection Abrasion Coating techniques Coatings Cotton fabrics Cotton fibers Magnesite Mechanical properties Particle size Particle size analysis Polyacrylates Polymers Rolls (machine components) Stiffness X ray spectrometers Roll coating Plastic coatings Magnesium Carbonate Mechanical Properties Particle Size |
Publisher: | Springer Netherlands | Abstract: | Abstract: In this study, cotton fiber fabrics were coated with polyacrylate-based polymer paste containing huntite–hydromagnesite by knife over roll process. The flame retardancy properties of the cotton fabrics were tested according to vertical flame test, limit oxygen index (LOI) test, smoldering cigarette and match flame tests. Thermal behavior of cotton fabrics was investigated by DTA–TG analysis. The antibacterial activities of coated cotton fabrics were qualitatively determined according to AATCC Method 147. Mechanical properties of cotton fabrics were evaluated with the help of tear strength, abrasion strength, thickness and stiffness measurements. Air permeability, UV protection and color properties were also investigated. Free formaldehyde content of the coatings on cotton fabrics were determined according to Japanese Law 112. The microstructural properties of cotton fabrics were characterized using SEM and FTIR (ATR) analysis. Furthermore, the mineral content and mean particle size value of huntite–hydromagnesite were also determined with X-ray fluorescence spectrometer and particle size analyzer. The flame retardancy and antibacterial properties of the cotton fabrics were improved after coating with acrylate-based polymer paste containing huntite–hydromagnesite. Mechanical properties such as tear strength of the cotton fabric decreased after coating process however huntite–hydromagnesite addition into coating paste did not lead to further increase on the tear strength loss of cotton fabric. Despite this, the resultant maximum abrasion cycles significantly increased following coating process application. Furthermore, colorimetric properties such as whiteness and lightness of cotton fabric did not significantly change after applied coating processes. SEM and FTIR analyses confirmed the constancy of microstructure of cotton fibers after coating process. Graphical abstract: [Figure not available: see fulltext.]. © 2018, Springer Nature B.V. | URI: | https://hdl.handle.net/11499/30280 https://doi.org/10.1007/s10570-018-1924-y |
ISSN: | 0969-0239 |
Appears in Collections: | Mühendislik Fakültesi Koleksiyonu Scopus İndeksli Yayınlar Koleksiyonu / Scopus Indexed Publications Collection WoS İndeksli Yayınlar Koleksiyonu / WoS Indexed Publications Collection |
Show full item record
CORE Recommender
SCOPUSTM
Citations
9
checked on Aug 17, 2024
WEB OF SCIENCETM
Citations
9
checked on Aug 1, 2024
Page view(s)
108
checked on Aug 24, 2024
Google ScholarTM
Check
Altmetric
Items in GCRIS Repository are protected by copyright, with all rights reserved, unless otherwise indicated.