Title: | The effect of high temperature gas carburizing on bending fatigue strength of SAE 8620 steel | Authors: | Asi, O. Can, Ahmet Çetin Pineault, J. Belassel, M. |
Keywords: | Applied loads Bending fatigues Case depths Equivalent loads Fatigue performance Fracture surfaces Gas carburizations Growth characteristics High temperature gas Metallographic examinations Retained austenites Rotating bending fatigues Scanning electron microscopes Ultrasonic baths X-ray diffraction techniques Carburizing Case hardening Gases Growth (materials) Scanning electron microscopy Steel Bending strength |
Abstract: | The bending fatigue performance of high temperature gas carburized SAE 8620 steel was evaluated and compared to conventional temperature gas carburization. To vary the case depth, different carburizing times were applied. The typical times were: 3 and 5 h at a temperature of 940 °C and 1 and 2 h at a temperature of 980 °C. To cause failure in the rotating bending fatigue specimens, the applied load was chosen as the equivalent load at 106 cycles when the material is subjected to bending fatigue. The characterization of residual stress and percent retained austenite in the specimens was performed using X-ray diffraction techniques; optical metallographic examination was also carried out. The fracture surfaces were cleaned in an ultrasonic bath and examined using a scanning electron microscope (SEM) equipped with EDX to evaluate the crack initiation and growth characteristics of the materials in the core and carburized case regions of the specimens. The results indicate that the fatigue performance of the high temperature gas carburized specimens was relatively poor compared to the conventionally gas carburized specimens. © 2008 Elsevier Ltd. All rights reserved. | URI: | https://hdl.handle.net/11499/6811 https://doi.org/10.1016/j.matdes.2008.07.020 |
ISSN: | 0264-1275 |
Appears in Collections: | Mühendislik Fakültesi Koleksiyonu Scopus İndeksli Yayınlar Koleksiyonu / Scopus Indexed Publications Collection WoS İndeksli Yayınlar Koleksiyonu / WoS Indexed Publications Collection |
Show full item record
CORE Recommender
SCOPUSTM
Citations
73
checked on Jan 4, 2025
WEB OF SCIENCETM
Citations
51
checked on Mar 7, 2025
Page view(s)
100
checked on Mar 4, 2025
Google ScholarTM
Check
Altmetric
Items in GCRIS Repository are protected by copyright, with all rights reserved, unless otherwise indicated.