Title: | The effect of extrusion and high-pressure torsion on the properties of Alumix-231 | Authors: | Ozdemir, I. Göde, Ceren Yilmazer, H. Çallıoğlu, Hasan |
Keywords: | Al-Si alloy EBSD Extrusion High-pressure torsion Mechanical properties Al-metal Eutectic silicon Extrusion ratio Hardness values High pressure torsions Hot extrusion Morphological changes Overall properties Properties and microstructures Quasihydrostatic pressure Refined microstructure Room temperature Rotation speed Severe plastic deformations XRD Aluminum Eutectics High pressure effects Hydrostatic pressure Microstructure Silicon alloys Torsional stress Tensile strength |
Abstract: | The mechanical properties and microstructure of commercial Al-15Si-2.5Cu-0.5Mg (Alumix-231 ®) alloy was subjected to extrusion (EXTR), hot extrusion into rods at 565°C at an extrusion ratio of 4:1 and high-pressure torsion (HPT) processing, one of the most severe plastic deformation (SPD) techniques, with an anvil rotation speed of 0.5rpm under a quasi-hydrostatic pressure of 5GPa. Afterwards, the microstructures of specimens were systematically investigated using XRD, SEM, EBSD, and TEM. Also, tensile properties of Alumix-231 processed by EXTR and HPT were determined at room temperature. The HPT specimen shows refined microstructure (around average 165nm) having more spherical and homogeneously distributed eutectic silicon second phases in Al metal matrix as compared to EXTR specimen. The hardness values are greater on the surface of the HPT specimen (239.1Hv) as compared to that EXTR specimen (71.2Hv) and increase with distance from the center of HPT specimen (198.3Hv). Tensile strength and ductility of HPT specimen increased approximately 2 times than that of EXTR sample, respectively. The results indicate that the morphological changes in eutectic silicon especially after HPT play a critical role in enhancing or limiting the overall properties of the Alumix-231 material. © 2011 Elsevier B.V. | URI: | https://hdl.handle.net/11499/8710 https://doi.org/10.1016/j.msea.2011.10.123 |
ISSN: | 0921-5093 |
Appears in Collections: | Denizli Teknik Bilimler Meslek Yüksekokulu Koleksiyonu Mühendislik Fakültesi Koleksiyonu Scopus İndeksli Yayınlar Koleksiyonu / Scopus Indexed Publications Collection WoS İndeksli Yayınlar Koleksiyonu / WoS Indexed Publications Collection |
Show full item record
CORE Recommender
Items in GCRIS Repository are protected by copyright, with all rights reserved, unless otherwise indicated.