Please use this identifier to cite or link to this item:
https://hdl.handle.net/11499/52251
Full metadata record
DC Field | Value | Language |
---|---|---|
dc.contributor.advisor | Aksöz, Sinan | en_US |
dc.contributor.advisor | Nimet Kardeş Sever | en_US |
dc.contributor.author | Karabudak, Ceylan | en_US |
dc.date.accessioned | 2023-08-24T07:20:42Z | - |
dc.date.available | 2023-08-24T07:20:42Z | - |
dc.date.issued | 2023 | en_US |
dc.identifier.uri | https://hdl.handle.net/11499/52251 | - |
dc.identifier.uri | https://tez.yok.gov.tr/UlusalTezMerkezi/TezGoster?key=a0OMTmEd_3mfOBxT8SiBTMjrOu7p1UdRPUPsSDSzUudsa9GY85mohFOXE3inhi4X | - |
dc.description | Bu tez çalışması PAMUKKALE ÜNİVERSİTESİ BİLİMSEL ARAŞTIRMA PROJELERİ KOORDİNASYON BİRİMİ tarafından 2022FEBE025 nolu proje ile desteklenmiştir. | en_US |
dc.description.abstract | Günümüzde, sahip oldukları benzersiz özellikler nedeniyle, şekil hafızalı alaşımların (ŞHA) kullanımı farklı teknik alanlarda giderek yaygınlaşmaya başlamıştır. Bu çalışmada; ŞHA’dan NiTi tozlarına, nadir toprak elementlerinden olan Neodimyum (Nd) ve Lantanyum (La) tozları MA yöntemi ile eklenmiştir. Numune üretimlerinde NiTi + ağ. %7, %10, %13 oranlarında Nd tozları ve NiTi + ağ. %1, %3, %5 oranlarında La tozları 300dk sürede mekanik öğütme ile ilave edilmiştir. Öğütülen tozlar ise NiTi+Nd toz karışımı için ~600 MPa basınç altında oda sıcaklığında preslenmiştir. Pres işleminden sonra numuneler kademeli olarak boro-sinterleme yöntemi kullanılarak, nihai sinterleme işlemi 1000°C’de 60dk olarak yapılmıştır. NiTi + La tozları ise ~450MPa basınçta oda sıcaklığında preslenmiş, kademeli olarak yapılan boro- sinterleme işlemi sonrasında nihai sinterleme 900°C ‘de 60dk sürede yapılmıştır. Tozların ve üretilen numunelerin sonrasında mikroyapı analizleri ve karakterizasyonu için Optik Mikroskop, FESEM, EDS, XRD ve DSC analizleri kullanılmıştır. NiTi + Nd numunelerinde ilave edilen Nd artışı ile martenzit başlangıç sıcaklığında ve sertlikte artış gözlenmiştir. Ayrıca NiTi + La tozlarına ilave edilen La oranının artması ile dönüşüm sıcaklığının kaybolduğu ve artan La oranına bağlı olarak sertlikte artışın olduğu gözlenmiştir. Boro-sinterleme yöntemiyle numuneler bor tuzunun içine yerleştirilerek, numunelerin oksitlenmeden ve homojen olarak sinterlenmesi sağlanmıştır. | en_US |
dc.description.abstract | Nowadays, due to the unique properties they have, the use of shape memory alloys has become increasingly widespread in different technical fields. In this study; Neodymium (Nd) and Lanthanum (La) powders, which are rare earth elements, were added to NiTi powders from SMA by MA method. In sample productions, NiTi+ wt 7%, 10%, %13 Nd powders and NiTi+wt 1%, 3%, 5% La powders added by mechanical grinding with 300 min. The ground powders were pressed at room temperature under ~600 MPa pressure of NiTi+Nd powder alloy. After pressing, the samples were boro-sintered gradually, and the final sintering process took 60 minutes at 1000°C. NiTi+La powders were pressed at room temperature at ~450MPa pressure, and after the gradual boro-sintering process, the final sintering took 60 minutes at 900°C. Optical Microscope, FESEM, EDS, XRD,DSC analyzes were used for microstructure analyses and characterization of powders and samples. An increase in martensite starting temperature and hardness was observed with the increase of Nd added in NiTi+Nd samples. In addition, it was observed that the transformation temperature dissappeared with the increase of La ratio added to NiTi+La powders, and an increase in hardness was observed depending on the increasing La ratio. By placing the samples in boron salt with boro-sintering method, the samples were sintered homogeneously and without oxidation. | en_US |
dc.language.iso | tr | en_US |
dc.rights | info:eu-repo/semantics/openAccess | en_US |
dc.subject | Şekil Hafızalı Alaşımlar | en_US |
dc.subject | NiTi Alaşımı | en_US |
dc.subject | Boro- Sinterleme | en_US |
dc.subject | Neodimyum | en_US |
dc.subject | Lantanyum | en_US |
dc.subject | Mekanik Öğütme | en_US |
dc.subject | Shape Memory Alloys | en_US |
dc.subject | NiTi Alloys | en_US |
dc.subject | Boro-Sintering | en_US |
dc.subject | Neodymium | en_US |
dc.subject | Lanthanum | en_US |
dc.subject | Mechanical Grinding | en_US |
dc.title | NİTİ+ND ve NİTİ+LA tozlarının mekanik öğütme sonrası boro-sinterleme yöntemi ile numune üretimi ve karakterizasyonu | en_US |
dc.title.alternative | Sample production and characterization of NITI+ND and NITI+LA powders by boro-sintering method after mechanical grinding | en_US |
dc.type | Master Thesis | en_US |
dc.department | PAÜ, Enstitüler, Fen Bilimleri Enstitüsü | en_US |
dc.relation.publicationcategory | Tez | en_US |
dc.identifier.yoktezid | 812218 | en_US |
dc.contributor.affiliation | Pamukkale Üniversitesi | en_US |
item.languageiso639-1 | tr | - |
item.fulltext | With Fulltext | - |
item.openairecristype | http://purl.org/coar/resource_type/c_18cf | - |
item.cerifentitytype | Publications | - |
item.openairetype | Master Thesis | - |
item.grantfulltext | open | - |
Appears in Collections: | Tez Koleksiyonu |
Files in This Item:
File | Description | Size | Format | |
---|---|---|---|---|
10406046.pdf | 4.86 MB | Adobe PDF | View/Open |
CORE Recommender
Page view(s)
142
checked on Aug 24, 2024
Download(s)
306
checked on Aug 24, 2024
Google ScholarTM
Check
Items in GCRIS Repository are protected by copyright, with all rights reserved, unless otherwise indicated.